 note = {application/pdf, Phase diagrams of Cr-H, Mn-H, Fe-H, Co-H and Ni-H alloys have been determined in the range of hydrogen pressures to ∼10 GPa and temperatures up to the melting point of the constituent metals. The dissolution of hydrogen causes appreciable reduction of the melting point and stabilization of close-packed structures, hcp, dhcp and fcc. The formation of superabundant vacancies (vacancyhydrogen clusters) was observed at high hydrogen pressures and high temperatures, and in the process of electrodeposition as well. Concomitant enhancement of metal-atom diffusion was also observed., 【査読有】},